Three reasons why PCB copper wires fall off

source:Industry News release time:2022-08-08 Article author:yu Popular:pcb


  Three reasons why PCB copper wires fall off(图1)

  1. Reasons for raw materials of PCB circuit board laminates:

  1. It is mentioned above that ordinary electrolytic copper foils are galvanized or copper-plated wool foil products. If the wool foil is produced with an abnormal peak value, or when galvanized/copper-plated, the coating dendrites are not good, causing the copper foil itself. The peel strength is not enough. After the poor foil pressed sheet is made into a PCB circuit board, when it is inserted in an electronic factory, the copper wire will fall off under the impact of external force. This kind of poor copper rejection will not cause obvious side etching after peeling the copper wire to see that the rough surface of the copper foil (that is, the surface in contact with the substrate), but the peeling strength of the copper foil on the whole surface will be very poor.

  2. Poor adaptability of copper foil and resin: Some laminates with special properties, such as HTg sheets, are currently used because of different resin systems. The curing agent used is generally PN resin, and the resin molecular chain structure is simple. When curing The degree of crosslinking is low, and it is necessary to use copper foil with special peaks to match it. When producing laminates, the use of copper foil does not match the resin system, resulting in insufficient peel strength of the metal-clad sheet metal foil, and poor copper wire falling off when inserting.

  2. Reasons for the PCB circuit board laminate process:

  Under normal circumstances, as long as the laminate is hot-pressed for more than 30 minutes in the high temperature section, the copper foil and the prepreg are basically completely combined, so the pressing generally does not affect the bonding force between the copper foil and the substrate in the laminate. However, in the process of stacking and stacking laminates, if PP is contaminated, or the rough surface of copper foil is damaged, it will also lead to insufficient bonding force between copper foil and substrate after lamination, resulting in positioning (only for large boards and language) or sporadic copper wires fall off, but there is no abnormality in the peeling strength of copper foil near the off-wire.

  , circuit board factory process factors:

  1. The PCB circuit design is unreasonable. Designing too thin circuits with thick copper foil will also cause excessive circuit etching and copper rejection.

  2. A local collision occurs in the production process of the PCB factory, and the copper wire is separated from the base material by external mechanical force. This defect is manifested as poor positioning or orientation, and there will be obvious twists in the dropped copper wire, or scratches/impact marks in the same direction. Peel off the bad copper wire and look at the rough surface of the copper foil. It can be seen that the color of the rough surface of the copper foil is normal, there will be no bad side corrosion, and the peeling strength of the copper foil is normal.

  3. The copper foil is over-etched. The electrolytic copper foils used in the market are generally single-sided galvanized (commonly known as ashing foil) and single-sided copper-plated (commonly known as reddish foil). Foils, red foils and ashing foils below 18um have basically not experienced batch copper rejection.

  When the customer's circuit is designed to pass the etching line, if the copper foil specification is changed but the etching parameters remain unchanged, the copper foil will stay in the etching solution for too long. Because zinc is an active metal, when the copper wire on the PCB is immersed in the etching solution for a long time, it will inevitably lead to excessive side etching of the circuit, causing the backing zinc layer of some thin circuits to be completely reacted and separated from the substrate. That is, the copper wire falls off.

  Another situation is that there is no problem with the etching parameters of the PCB circuit board, but the water washing and drying after etching are not good, causing the copper wire to be surrounded by the etching solution left on the PCB surface. Too much and throw copper. This situation is generally concentrated on thin lines, or during humid weather, similar defects will appear on the entire PCB. Strip the copper wire to see that the color of the contact surface with the base layer (the so-called roughened surface) has changed. The color of the copper foil is different from that of the normal copper foil. The original copper color of the bottom layer is seen, and the peeling strength of the copper foil at the thick circuit is also normal.


Read recommendations:

Six-layer Immersion Gold Board (BGA)

High frequency PCB

Six-layer Immersion Gold Board (BGA)

Six-layer Immersion Gold Board (BGA)

MCU PCB Processing

Previous:How many materials are there in the circuit board and what symbols are used to represent them? Back to list Next:PCB factory: multi-layer circuit board wiring method.Automotive Electronics PCB Wholesale

Online message

Popular recommended products

Related Information

PCB - the core building block of electronic products.Automotive Electronics PCB

2024-03-25

PCB - the bridge and link of the electronic world

2024-03-18

How to define high-frequency and high-precision circuit boards.Industrial Electronics PCB

2024-03-11

USB PCB interface layout and wiring requirements

2024-01-22

Electrolytic capacitor PCB.Steps for using PCB pins

2024-01-15

Automotive ElectronicWhat aspects should be considered when processing and manufacturing PCB boards?

2024-01-08

Electrolytic capaciWhat is the difference between a gold-plated circuit board and a gold-plated one?

2023-12-25

When grinding PCB boards, attention should be paid to.Oscillator (belonging to crystal) PCB

2023-12-18

Industrial Electronics PCB!What precautions should be taken when copying and grinding PCB boards

2023-12-11

Do you know who is more suitable for LED direct display, regarding the difference between PCB board

2023-12-05

Aluminum electrolytic capacitor PCB.What are the standards for selecting PCB boards

2023-11-27

Surface Mount Technology (SMT) Phase PCB

2023-11-20

Oscillator (belonging to crystal) PCB.The main functions of PCB board

2023-11-13

What is the difference between RO filter and PCB filter

2023-11-06

Method for determining blind hole PCB board

2023-11-01

Electronic Manufacturing Services PCB!What are the effects of PCB board color on performance?

2023-10-23

Introduction to the Manufacturing Steps and Requirements of PCBA Test Stand

2023-10-16

PCB version maturity stage.AOI circuit board price

2023-09-25

How to maintain a PCB circuit board

2023-09-19

Development Trend of Printed Circuit Board.Zener diode PCB Vendor

2023-09-14

Common problems and cause analysis of PCB circuit board sampling.Zener diode PCB price

2023-09-08

What are the issues that need to be understood in PCB circuit board design?IGBT module PCB factory

2023-09-08

How to reduce the risk of bending and deformation in PCB circuit board production?Inverter PCB Produ

2023-08-16

What are the three main factors that constitute welding defects in PCB circuit boards?Multilayer PCB

2023-08-16

The structure of a glass teapot.LCD Module PCB factory

2023-08-11

Glass teapot.Inverter PCB Processing

2023-08-11

PCB online debugging

2023-08-08

PCB offline programming

2023-08-08

What are the precautions for PCB design?

2023-07-27

Definition of Various Layers in PCB Circuit Board Design

2023-07-27